| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.890 g/cc | 0.890 g/cc | ISO 2782 | ||
| Viscosity Measurement | 19 @Temperature 150 °C | 19 @Temperature 302 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | ISO 868 | ||
| Tensile Strength | 9.40 MPa | 1360 psi | ISO 37 | ||
| Elongation at Break | 580 % | 580 % | ISO 37 | ||
| 100% Modulus | 0.00180 GPa | 0.261 ksi | ISO 37 | ||
| 200% Modulus | 0.00250 GPa | 0.363 ksi | ISO 37 | ||
| 300% Modulus | 0.00300 GPa | 0.435 ksi | ISO 37 | ||
| Tear Strength | 41.0 kN/m | 234 pli | ISO 34-B | ||
| Abrasion | 60 | 60 | mm3; DIN 53516 | ||
| Compression Set | 21 % @Temperature 22.0 °C, Time 259000 sec | 21 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
| 35 % @Temperature 70.0 °C, Time 79200 sec | 35 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 46 % @Temperature 100 °C, Time 79200 sec | 46 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Descriptive Properties | |||||
| Bonds with | Polypropylene | ||||
| Chemical Resistance | Acetone | Moderate/Good | |||
| Acids up to 80% | Excellent | ||||
| Alcohol | Excellent | ||||
| Alkalis | Excellent | ||||
| Brake fluid | Good | ||||
| Chlorinate solvents | Poor | ||||
| Diesel | Poor | ||||
| Ethylene glycol | Excellent | ||||
| Gasoline | Poor | ||||
| Salt solution | Excellent | ||||
| Soda lye | Excellent | ||||
| Water, 23°C | Excellent | ||||
| Water, 95°C | Good | ||||