- 拉伸强度 [MPa]: 6.48
- 脆化温度 [℃]: -64.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 55 | 55 | Instant; ASTM D2240 |
| Tensile Strength, Yield | 6.48 MPa | 940 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 3.24 MPa @Strain 300 % | 470 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 600 % | 600 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Rebound | 57 % | 57 % | Bayshore; ASTM D2632 |
| Tear Strength | 33.3 kN/m | 190 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 14 % | 14 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -64.0 °C | -83.2 °F | ASTM D746 |