- 密度 [g/cm3]: 1.16
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 96 | 96 | ASTM D2240 |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | DIN 53504 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 100% Modulus | 0.0154 GPa | 2.23 ksi | DIN 53504 |
| 300% Modulus | 0.0250 GPa | 3.63 ksi | DIN 53504 |
| Rebound | 30 % | 30 % | Bayshore; ASTM D2632 |
| Tear Strength | 147 kN/m | 840 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm3]; ISO 4649 |
| Compression Set | 32 % @Temperature 23.0 °C, Time 252000 sec | 32 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 50 % @Temperature 70.0 °C, Time 86400 sec | 50 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 185 - 200 °C | 365 - 392 °F | Huntsman/TMA |