- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 |
| Elongation at Break | 800 % | 800 % | ASTM D412 |
| 100% Modulus | 0.00550 GPa | 0.798 ksi | DIN 53504 |
| 300% Modulus | 0.0126 GPa | 1.83 ksi | DIN 53504 |
| Rebound | 36 % | 36 % | Bayshore; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm3]; ISO 4649 |
| Compression Set | 19 % @Temperature 23.0 °C, Time 252000 sec | 19 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 36 % @Temperature 70.0 °C, Time 86400 sec | 36 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 5.00e+8 ohm | 5.00e+8 ohm | antistat |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F | Huntsman/TMA |