- 密度 [g/cm3]: 1.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | DIN 53504 |
| Elongation at Break | 580 % | 580 % | ASTM D412 |
| 100% Modulus | 0.0114 GPa | 1.65 ksi | DIN 53504 |
| 300% Modulus | 0.0180 GPa | 2.61 ksi | DIN 53504 |
| Rebound | 41 % | 41 % | Bayshore; ASTM D2632 |
| Tear Strength | 130 kN/m | 740 pli | ASTM D624 |
| Abrasion | 20 | 20 | [mm3]; ISO 4649 |
| Compression Set | 14 % @Temperature 23.0 °C, Time 252000 sec | 14 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 26 % @Temperature 70.0 °C, Time 86400 sec | 26 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 180 - 195 °C | 356 - 383 °F | Huntsman/TMA |