- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.828
- 拉伸强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.14
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 4.9 % | 4.9 % | ASTM D638 |
| Tensile Modulus | 4.482 GPa | 650.0 ksi | 1 % Sec; ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | Tangent; ASTM D790 |
| Compressive Strength | 118 MPa | 17100 psi | ASTM D695 |
| Shear Strength | 52.4 MPa | 7600 psi | Ultimate; ASTM D3846 |
| Izod Impact, Notched | 0.828 J/cm | 1.55 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.18 | 0.18 | 1200 in/min, 155 lbs Load; ASTM D1894-95 |
| Limiting Pressure Velocity | 5.96 MPa-m/sec | 170000 psi-ft/min | 1200 in/min |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.90e+16 ohm-cm | 4.90e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.8 µm/m-°C @Temperature 20.0 °C | 26.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.245 W/m-K | 1.70 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 334 °C | 633 °F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |