- 熔体流动速率 [g/10min]: 45.5
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.44
- 拉伸强度 [MPa]: 91.0
- 弯曲模量 [MPa]: 3.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 Hours; ASTM D570 |
| Melt Flow | 45.5 - 91 g/10 min @Load 5.00 kg, Temperature 380 °C | 45.5 - 91 g/10 min @Load 11.0 lb, Temperature 716 °F | 6`; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 60 Hz | 2.8 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 60 Hz | 0.0030 @Frequency 60 Hz | ASTM D150 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C | 25.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Use; UL-746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | UL 94 |
| Oxygen Index | 40 % | 40 % | Limiting; ASTM D2863 |