- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.5
- 拉伸强度 [MPa]: 140.0
- 弯曲模量 [MPa]: 11.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.080 % | 0.080 % | 24 Hours; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 140 MPa | 20300 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 |
| Flexural Modulus | 11.1 GPa | 1610 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.4 µm/m-°C @Temperature 20.0 °C | 6.33 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Use; UL-746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ASTM D648 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 |
| Oxygen Index | 30 % | 30 % | Limiting; ASTM D2863 |