- 熔体流动速率 [g/10min]: 3.96
- 密度 [g/cm3]: 1.32
- 缺口冲击强度: 0.6
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 118 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | ISO 62 |
| Melt Flow | 3.96 - 13.2 g/10 min @Load 2.16 kg, Temperature 400 °C | 3.96 - 13.2 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 45 % | 45 % | ISO 527 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 93 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | IEC 243/1 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 260 °C | 500 °F | (Expected) Continuous use, UL |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |