- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 220.0
- 弯曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.080 % | 0.080 % | 24 Hours; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 220 MPa | 31900 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 22.0 GPa | 3190 ksi | ASTM D638 |
| Flexural Strength | 350 MPa | 50800 psi | ASTM D790 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 31.6 µm/m-°C @Temperature 20.0 °C | 17.6 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Use; UL-746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ASTM D648 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 |
| Oxygen Index | 45 % | 45 % | Limiting; ASTM D2863 |