- 密度 [g/cm3]: 1.42
- 缺口冲击强度: 9.0
- 弯曲模量 [MPa]: 12.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 162 MPa | 23500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.5 GPa | 1960 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 255 MPa | 37000 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 12.6 GPa | 1830 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.28 | 0.28 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1000 - 100000 ohm | 1000 - 100000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 9.50 µm/m-°C @Temperature 23.0 - 60.0 °C | 5.28 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 29.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |