- 密度 [g/cm3]: 1.37
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 87.0
- 断裂伸长率 [%]: 151
- 弯曲模量 [MPa]: 4.90
- 热变形温度 [℃]: 207.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 8.3 % | 8.3 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| Elongation at Yield | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 151 MPa | 21900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 21.7 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 27.2 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |