- 密度 [g/cm3]: 1.51
- 缺口冲击强度: 9.0
- 断裂伸长率 [%]: 215
- 弯曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.9 GPa | 1580 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 215 MPa | 31200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |