- 密度 [g/cm3]: 1.47
- 缺口冲击强度: 9.0
- 弯曲模量 [MPa]: 16.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 201 MPa | 29200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.5 GPa | 1960 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 267 MPa | 38700 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 16.3 GPa | 2360 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.700 mm | V-0 @Thickness 0.0276 in | UL 94 |