- 密度 [g/cm3]: 1.36
- 缺口冲击强度: 10.0
- 拉伸强度 [MPa]: 199.0
- 断裂伸长率 [%]: 280
- 弯曲模量 [MPa]: 13.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 199 MPa | 28900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Flexural Yield Strength | 280 MPa | 40600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.9 GPa | 2020 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |