- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.65
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Viscosity | 450000 cP | 450000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 3.70 GPa @Temperature 23.0 °C | 537 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 4.10 GPa @Temperature 23.0 °C | 595 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 0.650 kJ/m² @Temperature 23.0 °C | 0.309 ft-lb/in² @Temperature 73.4 °F | ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/U |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |