- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.45
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.300 g/cc | 0.0108 lb/in³ | ISO 1183 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Particle Size | 25 µm | 25 µm | D50; ISO 13320-1 |
| Viscosity | 150000 cP | 150000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Break | 15 % @Temperature 23.0 °C | 15 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 3.70 GPa @Temperature 23.0 °C | 537 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 170 MPa @Temperature 23.0 °C | 24700 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 4.10 GPa @Temperature 23.0 °C | 595 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 0.450 kJ/m² @Temperature 23.0 °C | 0.214 ft-lb/in² @Temperature 73.4 °F | ISO 180/A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/U |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 380 - 400 °C | 716 - 752 °F | |
| Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | ||