TPV 3140物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Viscosity | 253000 cP @Shear Rate 206 1/s, Temperature 200 °C |
253000 cP @Shear Rate 206 1/s, Temperature 392 °F |
ASTM D3835 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 37 | 37 | extruded sample; 5 sec. delay; ASTM D2240 |
| 43 | 43 | injection molded sample; 5 sec. delay; ASTM D2240 | |
| Tensile Strength at Break | 2.10 MPa | 305 psi | Die C; Flow direction; ASTM D412 |
| 3.10 MPa | 450 psi | Die C; Cross direction; ASTM D412 | |
| Elongation at Break | 263 % | 263 % | Die C; Flow direction; ASTM D412 |
| 474 % | 474 % | Die C; Cross direction; ASTM D412 | |
| 100% Modulus | 0.00100 GPa | 0.145 ksi | Die C; Cross direction; ASTM D412 |
| 0.00130 GPa | 0.189 ksi | Die C; Flow direction; ASTM D412 | |
| Tear Strength | 16.0 kN/m | 91.3 pli | Die C; Cross direction; ASTM D624 |
| Compression Set | 31 % | 31 % | 22h/23°C; ASTM D395B |
| 41 % @Temperature 100 °C |
41 % @Temperature 212 °F |
22hr; ASTM D395B | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 182 - 204 °C | 360 - 400 °F | Extrusion |
| 177 - 216 °C | 350 - 420 °F | Injection Molding | |
| Middle Barrel Temperature | 182 - 204 °C | 360 - 400 °F | Extrusion Transition Zone |
| 177 - 216 °C | 350 - 420 °F | Injection Molding | |
| 188 - 210 °C | 370 - 410 °F | Extrusion Metering Zone | |
| Front Barrel Temperature | 177 - 216 °C | 350 - 420 °F | Injection Molding |
| 188 - 210 °C | 370 - 410 °F | Extrusion | |
| Nozzle Temperature | 188 - 221 °C | 370 - 430 °F | Injection Molding |
| Die Temperature | 193 - 216 °C | 380 - 420 °F | Extrusion |
| Melt Temperature | 182 - 221 °C | 360 - 430 °F | Injection Molding |
| 193 - 216 °C | 380 - 420 °F | Extrusion | |
| Mold Temperature | 10.0 - 65.6 °C | 50.0 - 150 °F | Injection Molding |
| Roll Temperature | 21.1 - 48.9 °C | 70.0 - 120 °F | Extrusion |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 0.0689 - 1.03 MPa | 10.0 - 150 psi | Injection Molding Back Pressure |
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。
广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管等、、、、