PA6 8272G HS BK-102 12%玻璃、_产品资讯

PA6 8272G 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.22 g/cc	0.0441 lb/in³	ISO 1183
Water Absorption	1.4 %	1.4 %	24 hour; ISO Test
	8.3 %	8.3 %	ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM Test
Tensile Strength at Break	110 MPa	16000 psi	0.2 in/min; ASTM Test
	45.0 MPa @Temperature 120 °C	6530 psi @Temperature 248 °F	ASTM Test
	45.0 MPa @Temperature 120 °C	6530 psi @Temperature 248 °F	ISO Data
	115 MPa @Temperature -40.0 °C	16700 psi @Temperature -40.0 °F	ISO Data
	115 MPa @Temperature -40.0 °C	16700 psi @Temperature -40.0 °F	ASTM Test
Tensile Strength, Ultimate	110 MPa	16000 psi	5mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5mm/min; ISO 527
	3.0 %	3.0 %	0.2 in/min; ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ISO Data
	15 % @Temperature 120 °C	15 % @Temperature 248 °F	ISO Data
	15 % @Temperature 120 °C	15 % @Temperature 248 °F	ASTM Test
Tensile Modulus	5.22 GPa	757 ksi	1mm/min; ISO 527
	1.445 GPa @Temperature 120 °C	209.6 ksi @Temperature 248 °F	ISO Data
	2.10 GPa @Temperature 80.0 °C	305 ksi @Temperature 176 °F	ISO Data
	6.37 GPa @Temperature -40.0 °C	924 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	165 MPa	23900 psi	ASTM Test
	50.0 MPa @Temperature 120 °C	7250 psi @Temperature 248 °F	ASTM Test
	200 MPa @Temperature -40.0 °C	29000 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	4.30 GPa	624 ksi	ISO Data
	4.65 GPa	674 ksi	ASTM Test
	0.995 GPa @Temperature 120 °C	144 ksi @Temperature 248 °F	ASTM Test
Izod Impact, Notched	0.400 J/cm @Temperature -40.0 °C	0.749 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.450 J/cm @Thickness 3.17 mm	0.843 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	5.90 kJ/m²	2.81 ft-lb/in²	ISO Test
Charpy Impact, Notched	0.710 J/cm²	3.38 ft-lb/in²	ISO 179

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093

Thermal Properties	Metric	English	Comments
CTE, linear	97.0 µm/m-°C @Temperature -30.0 - 30.0 °C	53.9 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
CTE, linear, Parallel to Flow	28.0 µm/m-°C	15.6 µin/in-°F	ISO 11359
CTE, linear, Transverse to Flow	72.0 µm/m-°C	40.0 µin/in-°F	ISO 11359
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	170 °C	338 °F	ISO 75
	197 °C	387 °F	ASTM Test

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties
Color	BK-102
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Blow Molding
Processing	Blow molding
	Injection Molding
Special characteristic	Heat stabilized or stable to heat

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。