物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | ISO 62 | ||
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | conditioned; ISO 2039-1 | ||
| 185 MPa | 26800 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 | ||
| 165 MPa | 23900 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 8.0 % | 8.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 4.80 GPa | 696 ksi | conditioned; ISO 527-1/-2 | ||
| 8.50 GPa | 1230 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | dry; ISO 179/1eU | ||
| 8.50 J/cm² | 40.4 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| 7.00 J/cm² @Temperature 30.0 °C |
33.3 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | dry; ISO 179/1eA | ||
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.900 J/cm² @Temperature 30.0 °C |
4.28 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| 0.900 J/cm² @Temperature 30.0 °C |
4.28 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | conditioned; IEC 60243-1 | ||
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 575 V | 575 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS | ||
| 160 °C | 320 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| De |
|||||
| Automotive | Air intake sytems | ||||
| Interior | |||||
| Electricals & Electronics | Electrical appliances | ||||
| Electrical equipment | |||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||