类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋
材料说明：极低排放的高粘度缩醛均聚物
聚甲醛100pe bk602（原de20573）是一种高粘度缩醛均聚物增强版的Delrin 100P具有非常低的挥发性有机化合物的排放。它有一个巨大的力量和韧性的组合
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |||
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |||
| Linear Mold Shrinkage, Flow | 0.022 cm/cm | 0.022 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 | ||
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm³/10min; ISO 1133 | ||
| 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.6 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 92 | 92 | ISO 2039-2 | ||
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 | ||
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 32 % | 32 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 21 % | 21 % | ISO 527-1/-2 | ||
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 80.0 MPa @Strain 3.50 % |
11600 psi @Strain 3.50 % |
ISO 178 | ||
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 35.0 J/cm² | 167 ft-lb/in² | ISO 179/1eU | ||
| 30.0 J/cm² @Temperature -30.0 °C |
143 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 5.00e+13 ohm | 5.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | ||
| 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 44.0 kV/mm | 1120 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00050 @Frequency 100 Hz |
0.00050 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0055 @Frequency 1.00e+6 Hz |
0.0055 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| 100 µm/m-°C @Temperature -40.0 - 23.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ISO 75-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Emissions | <2 mg/kg | VDA 275 | |||
| Part Marking Code | >POM< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Other Extrusion | |||||
| Profile Extrusion | |||||
| Sheet Extrusion | |||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM | ISO 1043 |
|||