Physical Properties Metric English Comments
Density  1.31 g/cc 0.0473 lb/in³  
  1.34 g/cc 0.0484 lb/in³ DAM; ISO 1183
Water Absorption  6.2 %
@Thickness 2.00 mm		 6.2 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Moisture Absorption  1.80 %
@Thickness 2.00 mm		 1.80 %
@Thickness 0.0787 in		 DAM; Sim. to ISO 62
Viscosity   67600 cP
@Shear Rate 5000 1/s,
Temperature 280 °C		 67600 cP
@Shear Rate 5000 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  76791 cP
@Shear Rate 5000 1/s,
Temperature 270 °C		 76791 cP
@Shear Rate 5000 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  88000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 88000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  220700 cP
@Shear Rate 500 1/s,
Temperature 280 °C		 220700 cP
@Shear Rate 500 1/s,
Temperature 536 °F		 ISO 11403-1 -2
  260300 cP
@Shear Rate 500 1/s,
Temperature 270 °C		 260300 cP
@Shear Rate 500 1/s,
Temperature 518 °F		 ISO 11403-1 -2
  308100 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 308100 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
Viscosity Test  135 cm³/g 135 cm³/g DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.0020 cm/cm 0.0020 in/in DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.010 cm/cm 0.010 in/in DAM; ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  110 MPa 16000 psi 50%RH; ISO 527-1/-2
  170 MPa 24700 psi DAM; ISO 527-1/-2
Tensile Stress  18.4 MPa
@Strain 0.550 %,
Temperature 150 °C		 2670 psi
@Strain 0.550 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  20.9 MPa
@Strain 0.550 %,
Temperature 90.0 °C		 3030 psi
@Strain 0.550 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  29.5 MPa
@Strain 0.450 %,
Temperature 40.0 °C		 4280 psi
@Strain 0.450 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  33.7 MPa
@Strain 0.340 %,
Temperature -20.0 °C		 4890 psi
@Strain 0.340 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  34.1 MPa
@Strain 0.400 %,
Temperature 23.0 °C		 4950 psi
@Strain 0.400 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  34.9 MPa
@Strain 0.730 %,
Temperature 23.0 °C		 5060 psi
@Strain 0.730 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  36.3 MPa
@Strain 0.380 %,
Temperature 0.000 °C		 5260 psi
@Strain 0.380 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  44.5 MPa
@Strain 2.20 %,
Temperature 150 °C		 6450 psi
@Strain 2.20 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  54.5 MPa
@Strain 2.20 %,
Temperature 90.0 °C		 7900 psi
@Strain 2.20 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  58.7 MPa
@Strain 4.95 %,
Temperature 150 °C		 8510 psi
@Strain 4.95 %,
Temperature 302 °F		 DAM; ISO 11403-1 -2
  69.9 MPa
@Strain 3.85 %,
Temperature 90.0 °C		 10100 psi
@Strain 3.85 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  81.2 MPa
@Strain 5.50 %,
Temperature 90.0 °C		 11800 psi
@Strain 5.50 %,
Temperature 194 °F		 DAM; ISO 11403-1 -2
  88.6 MPa
@Strain 2.92 %,
Temperature 23.0 °C		 12900 psi
@Strain 2.92 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  92.0 MPa
@Strain 1.80 %,
Temperature 40.0 °C		 13300 psi
@Strain 1.80 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  103 MPa
@Strain 5.84 %,
Temperature 23.0 °C		 14900 psi
@Strain 5.84 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  116 MPa
@Strain 1.60 %,
Temperature 23.0 °C		 16800 psi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  120 MPa
@Strain 3.15 %,
Temperature 40.0 °C		 17400 psi
@Strain 3.15 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  122 MPa
@Strain 1.36 %,
Temperature -20.0 °C		 17700 psi
@Strain 1.36 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  127 MPa
@Strain 1.52 %,
Temperature 0.000 °C		 18400 psi
@Strain 1.52 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  156 MPa
@Strain 2.80 %,
Temperature 23.0 °C		 22600 psi
@Strain 2.80 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  177 MPa
@Strain 2.66 %,
Temperature 0.000 °C		 25700 psi
@Strain 2.66 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  182 MPa
@Strain 2.38 %,
Temperature -20.0 °C		 26400 psi
@Strain 2.38 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  189 MPa
@Strain 3.80 %,
Temperature 0.000 °C		 27400 psi
@Strain 3.80 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  207 MPa
@Strain 3.40 %,
Temperature -20.0 °C		 30000 psi
@Strain 3.40 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
Elongation at Break  3.0 % 3.0 % DAM; ISO 527-1/-2
  6.0 % 6.0 % 50%RH; ISO 527-1/-2
Tensile Modulus  5.70 GPa 827 ksi 50%RH; ISO 527-1/-2
  9.10 GPa 1320 ksi DAM; ISO 527-1/-2
Flexural Modulus  5.70 GPa 827 ksi 50%RH; ISO 178
  9.00 GPa 1310 ksi DAM; ISO 178
Shear Modulus   0.5372 GPa
@Temperature 150 °C		 77.92 ksi
@Temperature 302 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.5783 GPa
@Temperature 110 °C		 83.88 ksi
@Temperature 230 °F		 DAM; Dynamic; ISO 11403-1 -2
  0.8342 GPa
@Temperature 60.0 °C		 121.0 ksi
@Temperature 140 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.7163 GPa
@Temperature 10.0 °C		 248.93 ksi
@Temperature 50.0 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.7688 GPa
@Temperature -20.0 °C		 256.55 ksi
@Temperature -4.00 °F		 DAM; Dynamic; ISO 11403-1 -2
  1.9299 GPa
@Temperature -50.0 °C		 279.91 ksi
@Temperature -58.0 °F		 DAM; Dynamic; ISO 11403-1 -2
Secant Modulus   3.03 GPa
@Strain 2.92 %,
Temperature 23.0 °C		 440 ksi
@Strain 2.92 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  3.42 GPa
@Strain 3.60 %,
Temperature 40.0 °C		 496 ksi
@Strain 3.60 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  4.78 GPa
@Strain 0.730 %,
Temperature 23.0 °C		 693 ksi
@Strain 0.730 %,
Temperature 73.4 °F		 50%RH; ISO 11403-1 -2
  5.00 GPa
@Strain 3.20 %,
Temperature 23.0 °C		 725 ksi
@Strain 3.20 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  5.11 GPa
@Strain 1.80 %,
Temperature 40.0 °C		 741 ksi
@Strain 1.80 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  6.09 GPa
@Strain 3.04 %,
Temperature 0.000 °C		 883 ksi
@Strain 3.04 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  6.56 GPa
@Strain 0.450 %,
Temperature 40.0 °C		 951 ksi
@Strain 0.450 %,
Temperature 104 °F		 DAM; ISO 11403-1 -2
  7.13 GPa
@Strain 2.72 %,
Temperature -20.0 °C		 1030 ksi
@Strain 2.72 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  7.25 GPa
@Strain 1.60 %,
Temperature 23.0 °C		 1050 ksi
@Strain 1.60 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.36 GPa
@Strain 1.52 %,
Temperature 0.000 °C		 1210 ksi
@Strain 1.52 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  8.525 GPa
@Strain 0.400 %,
Temperature 23.0 °C		 1236 ksi
@Strain 0.400 %,
Temperature 73.4 °F		 DAM; ISO 11403-1 -2
  8.97 GPa
@Strain 1.36 %,
Temperature -20.0 °C		 1300 ksi
@Strain 1.36 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
  9.55 GPa
@Strain 0.380 %,
Temperature 0.000 °C		 1390 ksi
@Strain 0.380 %,
Temperature 32.0 °F		 DAM; ISO 11403-1 -2
  9.91 GPa
@Strain 0.340 %,
Temperature -20.0 °C		 1440 ksi
@Strain 0.340 %,
Temperature -4.00 °F		 DAM; ISO 11403-1 -2
Izod Impact, Notched (ISO)  17.0 kJ/m² 8.09 ft-lb/in² DAM; ISO 180/1A
  24.0 kJ/m² 11.4 ft-lb/in² 50%RH; ISO 180/1A
  12.0 kJ/m²
@Temperature -30.0 °C		 5.71 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 180/1A
  12.0 kJ/m²
@Temperature -30.0 °C		 5.71 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  80.0 kJ/m² 38.1 ft-lb/in² DAM; ISO 180/1U
  80.0 kJ/m² 38.1 ft-lb/in² 50%RH; ISO 180/1U
Charpy Impact Unnotched  10.0 J/cm² 47.6 ft-lb/in² DAM; ISO 179/1eU
  10.0 J/cm² 47.6 ft-lb/in² 50%RH; ISO 179/1eU
  9.40 J/cm²
@Temperature -30.0 °C		 44.7 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eU
  10.0 J/cm²
@Temperature -30.0 °C		 47.6 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eU
Charpy Impact, Notched  2.00 J/cm² 9.52 ft-lb/in² DAM; ISO 179/1eA
  2.50 J/cm² 11.9 ft-lb/in² 50%RH; ISO 179/1eA
  1.20 J/cm²
@Temperature -30.0 °C		 5.71 ft-lb/in²
@Temperature -22.0 °F		 50%RH; ISO 179/1eA
  1.30 J/cm²
@Temperature -30.0 °C		 6.19 ft-lb/in²
@Temperature -22.0 °F		 DAM; ISO 179/1eA
 
Electrical Properties Metric English Comments
Comparative Tracking Index  550 V 550 V DAM; IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  28.0 µm/m-°C 15.6 µin/in-°F DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F DAM; ISO 11359-1/-2
Specific Heat Capacity  2.20 J/g-°C 0.526 BTU/lb-°F  
Thermal Conductivity  0.230 W/m-K 1.60 BTU-in/hr-ft²-°F of melt
Melting Point  221 °C 430 °F DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  221 °C 430 °F DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  210 °C 410 °F DAM; ISO 75-1/-2
Vicat Softening Point  215 °C 419 °F DAM; 50°C/h 50N; ISO 306
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 DAM; IEC 60695-11-10
Flame Spread  22 mm/min
@Thickness 1.00 mm		 0.87 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PA6-IGF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PA6-IGF30  
UL recognition UL DAM

概述

PA塑料(尼龙，聚酰胺)，英文名称:Polyamide

PA的品种繁多，有PA6、PA66、PAll、PAl2、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等很多新品种。

物理性能

比重：PA6 1.14克/立方厘米，PA66 1.15克/立方厘米，PA1010 1.05克/立方厘米

成型收缩率：PA6 0.8-2.5% ，PA66 1.5-2.2%

成型温度：220-300℃

干燥条件：100-110℃/12小时

坚韧、耐磨、耐油、,耐水、抗酶菌、但吸水大

燃烧鉴别方法：火焰上端黄色，下端蓝色，燃烧后塑料熔滴落，起泡，离火后特殊的羊毛，指甲烧焦味和带芹菜味

尼龙6：

弹性好，冲击强度，吸水较大

尼龙66：

性能优于尼龙6，强度高，耐磨性好

尼龙610：

与尼龙66相似，但吸水小，刚度低

尼龙1010：

半透明，吸水小。耐寒性较好。适于制作一般机械零件、减磨耐磨零件、传动零件以及化工、电器、仪表等零件

成型性能

1、结晶料，熔点较高，熔融温度范围窄，热稳定性差，料温超过300度、滞留时间超过30分钟即分解。较易吸湿，需干燥，含水量不得超过0.3%。

2、流动性好，易溢料。宜用自锁时喷嘴，并应加热。

3、成型收缩范围及收缩率大，方向性明显，易发生缩孔、变形等。

4、模温按塑件壁厚在20～90度范围内选取，注射压力按注射机类型、料温、塑件形状尺寸、模具浇注系统选定，成型周期按塑件壁厚选定。树脂粘度小时，注射、冷却时间应取长，并用白油作脱模剂。

5、模具浇注系统的形式和尺寸，增大流道和浇口尺寸可减少缩水。

聚酰胺的不足之处在于：由于热膨胀和吸水性所至的尺寸精度不够，耐酸性差，硬度和弹性模量不够。经改良以后，也是比较优秀的工程塑料之一。

应用

汽车制造方面

用于制造燃料滤网、燃料过滤器、罐、捕集器、储油槽、发动机汽缸盖罩、散热器水缸、平衡旋转轴齿轮。也可用在汽车的电器配件、接线柱等。另外，它还可用作驱动、控制部件等。

电器电子工业

可用于制造电饭锅、电动吸尘器、高频电子食品加热器，电器产品的接线柱、开关和电阻器等。

医疗器械仪器

用于医用输血管、取血器、输液器等。PA单丝可做外科手术缝线、假发等；另外，电子打字机的数字旋转盘、接线柱、传动齿轮、印刷机的带式过滤片等。

其它方面

用于制作一次性打火机体、碱性干电池衬垫，摩托车驾驶员的头盔，办公机器外壳，办公用椅的角轮、座和靠背，冰鞋、钓鱼线等，PA薄膜气体阻隔性能优良，而且耐油性、耐低温冲击性、耐穿透性好，可用于肉、火腿肠等冷冻食品的包装。聚酰胺还可棒材和板材，也作齿轮或其它传动装置。

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-39813.html

免责声明: 本文 PA6/美国杜邦/73G30T NC010 耐磨 注塑级 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4