| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.35 % @Thickness 2.00 mm |
0.35 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.150 % @Thickness 2.00 mm |
0.150 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Viscosity | 230000 cP @Temperature 250 °C |
230000 cP @Temperature 482 °F |
@ 1000 sec-1; ISO 11443 | ||
| 68400 cP @Shear Rate 5000 1/s, Temperature 270 °C |
68400 cP @Shear Rate 5000 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 81500 cP @Shear Rate 5000 1/s, Temperature 260 °C |
81500 cP @Shear Rate 5000 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| 98700 cP @Shear Rate 5000 1/s, Temperature 250 °C |
98700 cP @Shear Rate 5000 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| 211600 cP @Shear Rate 500 1/s, Temperature 270 °C |
211600 cP @Shear Rate 500 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |||
| 253100 cP @Shear Rate 500 1/s, Temperature 260 °C |
253100 cP @Shear Rate 500 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |||
| 300300 cP @Shear Rate 500 1/s, Temperature 250 °C |
300300 cP @Shear Rate 500 1/s, Temperature 482 °F |
ISO 11403-1 -2 | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 2577 | ||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 | ||
| Tensile Stress | 8.01 MPa @Strain 0.240 %, Temperature 150 °C |
1160 psi @Strain 0.240 %, Temperature 302 °F |
ISO 11403-1 -2 | ||
| 10.04 MPa @Strain 0.210 %, Temperature 90.0 °C |
1456 psi @Strain 0.210 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 23.3 MPa @Strain 0.330 %, Temperature 40.0 °C |
3380 psi @Strain 0.330 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 26.61 MPa @Strain 1.05 %, Temperature 150 °C |
3859 psi @Strain 1.05 %, Temperature 302 °F |
ISO 11403-1 -2 | |||
| 32.96 MPa @Strain 0.360 %, Temperature 23.0 °C |
4780 psi @Strain 0.360 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 33.14 MPa @Strain 0.830 %, Temperature 90.0 °C |
4807 psi @Strain 0.830 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 37.33 MPa @Strain 1.98 %, Temperature 150 °C |
5414 psi @Strain 1.98 %, Temperature 302 °F |
ISO 11403-1 -2 | |||
| 43.6 MPa @Strain 2.96 %, Temperature 150 °C |
6320 psi @Strain 2.96 %, Temperature 302 °F |
ISO 11403-1 -2 | |||
| 43.81 MPa @Strain 0.440 %, Temperature 0.000 °C |
6354 psi @Strain 0.440 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 49.22 MPa @Strain 1.53 %, Temperature 90.0 °C |
7139 psi @Strain 1.53 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 57.24 MPa @Strain 0.960 %, Temperature 40.0 °C |
8302 psi @Strain 0.960 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 59.41 MPa @Strain 2.26 %, Temperature 90.0 °C |
8617 psi @Strain 2.26 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 65.44 MPa @Strain 0.660 %, Temperature -20.0 °C |
9491 psi @Strain 0.660 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 66.81 MPa @Strain 0.790 %, Temperature 23.0 °C |
9690 psi @Strain 0.790 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 74.56 MPa @Strain 0.790 %, Temperature 0.000 °C |
10810 psi @Strain 0.790 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 76.98 MPa @Strain 1.51 %, Temperature 40.0 °C |
11170 psi @Strain 1.51 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 84.73 MPa @Strain 0.790 %, Temperature -40.0 °C |
12290 psi @Strain 0.790 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 91.45 MPa @Strain 1.21 %, Temperature 23.0 °C |
13260 psi @Strain 1.21 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 91.85 MPa @Strain 2.14 %, Temperature 40.0 °C |
13320 psi @Strain 2.14 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 103.45 MPa @Strain 1.19 %, Temperature 0.000 °C |
15004 psi @Strain 1.19 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 110.95 MPa @Strain 1.68 %, Temperature 23.0 °C |
16092 psi @Strain 1.68 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 121.04 MPa @Strain 1.33 %, Temperature -20.0 °C |
17555 psi @Strain 1.33 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 122.73 MPa @Strain 1.21 %, Temperature -40.0 °C |
17801 psi @Strain 1.21 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 128.42 MPa @Strain 1.66 %, Temperature 0.000 °C |
18626 psi @Strain 1.66 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 159.43 MPa @Strain 2.06 %, Temperature -20.0 °C |
23123 psi @Strain 2.06 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 168.02 MPa @Strain 1.85 %, Temperature -40.0 °C |
24369 psi @Strain 1.85 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 198.29 MPa @Strain 2.50 %, Temperature -40.0 °C |
28760 psi @Strain 2.50 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Elongation at Break | 3.1 % | 3.1 % | ISO 527-1/-2 | ||
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 195 MPa | 28300 psi | ISO 178 | ||
| Secant Modulus | 3.76 GPa @Strain 2.64 %, Temperature 40.0 °C |
545 ksi @Strain 2.64 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
| 4.83 GPa @Strain 1.71 %, Temperature 40.0 °C |
701 ksi @Strain 1.71 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 5.91 GPa @Strain 2.05 %, Temperature 23.0 °C |
857 ksi @Strain 2.05 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 5.9625 GPa @Strain 0.960 %, Temperature 40.0 °C |
864.80 ksi @Strain 0.960 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 6.98 GPa @Strain 2.05 %, Temperature 0.000 °C |
1010 ksi @Strain 2.05 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 7.06 GPa @Strain 0.330 %, Temperature 40.0 °C |
1020 ksi @Strain 0.330 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 7.25 GPa @Strain 1.36 %, Temperature 23.0 °C |
1050 ksi @Strain 1.36 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 7.33 GPa @Strain 2.30 %, Temperature -20.0 °C |
1060 ksi @Strain 2.30 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 8.40 GPa @Strain 1.34 %, Temperature 0.000 °C |
1220 ksi @Strain 1.34 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 8.46 GPa @Strain 0.790 %, Temperature 23.0 °C |
1230 ksi @Strain 0.790 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 8.68 GPa @Strain 2.06 %, Temperature -40.0 °C |
1260 ksi @Strain 2.06 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 9.10 GPa @Strain 1.33 %, Temperature -20.0 °C |
1320 ksi @Strain 1.33 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 9.16 GPa @Strain 0.360 %, Temperature 23.0 °C |
1330 ksi @Strain 0.360 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 9.44 GPa @Strain 0.790 %, Temperature 0.000 °C |
1370 ksi @Strain 0.790 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 9.92 GPa @Strain 0.660 %, Temperature -20.0 °C |
1440 ksi @Strain 0.660 %, Temperature -4.00 °F |
ISO 11403-1 -2 | |||
| 9.96 GPa @Strain 0.440 %, Temperature 0.000 °C |
1440 ksi @Strain 0.440 %, Temperature 32.0 °F |
ISO 11403-1 -2 | |||
| 10.143 GPa @Strain 1.21 %, Temperature -40.0 °C |
1471.1 ksi @Strain 1.21 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| 10.7 GPa @Strain 0.790 %, Temperature -40.0 °C |
1560 ksi @Strain 0.790 %, Temperature -40.0 °F |
ISO 11403-1 -2 | |||
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -40.0 °C |
4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 65.0 °C | 149 °F | 10°C/min; ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| Flame Spread | 30 mm/min @Thickness 1.00 mm |
1.2 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PBT-IGF30< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PBT-IGF30 | ||||
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。
⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。
⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。
⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。
⒋耐溶剂好，无应力开裂。
⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。
⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。
⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。
⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。
PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。
优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；
3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。
用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；
2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；
3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。
特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.
上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！
可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：
联系人：邓小姐
联系电话：13917657923
联系QQ:996152797
联系邮箱：996152797@qq.com