  4. PBT/美国杜邦/S600F20 NC010 中粘 高流动

PBT/美国杜邦/S600F20 NC010 中粘 高流动

PBT/美国杜邦/S600F20 NC010 中粘 高流动
 参考图片：

颗粒图片：

包装图片：

成品图片：
19-44-36-87-342874.jpg.middle

 

 

 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.31 g/cc 0.0473 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   88500 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 88500 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  98730 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 98730 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  109800 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 109800 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  239900 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 239900 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  303800 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 303800 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  384600 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 384600 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  130 cm³/g 130 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow  19.1 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 19.1 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   2.81 MPa
@Strain 1.14 %,
Temperature 150 °C		 408 psi
@Strain 1.14 %,
Temperature 302 °F		 ISO 11403-1 -2
  2.88 MPa
@Strain 0.190 %,
Temperature 40.0 °C		 418 psi
@Strain 0.190 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.32 MPa
@Strain 1.04 %,
Temperature 90.0 °C		 627 psi
@Strain 1.04 %,
Temperature 194 °F		 ISO 11403-1 -2
  6.84 MPa
@Strain 4.36 %,
Temperature 150 °C		 992 psi
@Strain 4.36 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.06 MPa
@Strain 7.90 %,
Temperature 150 °C		 1310 psi
@Strain 7.90 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.31 MPa
@Strain 0.350 %,
Temperature 23.0 °C		 1350 psi
@Strain 0.350 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  11.7 MPa
@Strain 3.92 %,
Temperature 90.0 °C		 1700 psi
@Strain 3.92 %,
Temperature 194 °F		 ISO 11403-1 -2
  16.07 MPa
@Strain 6.99 %,
Temperature 90.0 °C		 2331 psi
@Strain 6.99 %,
Temperature 194 °F		 ISO 11403-1 -2
  17.7 MPa
@Strain 0.630 %,
Temperature 0.000 °C		 2570 psi
@Strain 0.630 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  18.6 MPa
@Strain 10.5 %,
Temperature 90.0 °C		 2700 psi
@Strain 10.5 %,
Temperature 194 °F		 ISO 11403-1 -2
  21.96 MPa
@Strain 2.10 %,
Temperature 40.0 °C		 3185 psi
@Strain 2.10 %,
Temperature 104 °F		 ISO 11403-1 -2
  25.21 MPa
@Strain 0.790 %,
Temperature -40.0 °C		 3656 psi
@Strain 0.790 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  25.36 MPa
@Strain 0.860 %,
Temperature -20.0 °C		 3678 psi
@Strain 0.860 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  30.59 MPa
@Strain 5.18 %,
Temperature 40.0 °C		 4437 psi
@Strain 5.18 %,
Temperature 104 °F		 ISO 11403-1 -2
  34.8 MPa
@Strain 8.60 %,
Temperature 40.0 °C		 5050 psi
@Strain 8.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  42.45 MPa
@Strain 1.89 %,
Temperature 23.0 °C		 6157 psi
@Strain 1.89 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  46.64 MPa
@Strain 1.82 %,
Temperature 0.000 °C		 6765 psi
@Strain 1.82 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  53.41 MPa
@Strain 1.85 %,
Temperature -40.0 °C		 7746 psi
@Strain 1.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  57.12 MPa
@Strain 2.19 %,
Temperature -20.0 °C		 8285 psi
@Strain 2.19 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  66.69 MPa
@Strain 3.74 %,
Temperature 0.000 °C		 9673 psi
@Strain 3.74 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.3 MPa
@Strain 2.85 %,
Temperature -40.0 °C		 10600 psi
@Strain 2.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  78.69 MPa
@Strain 4.18 %,
Temperature -20.0 °C		 11410 psi
@Strain 4.18 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  88.18 MPa
@Strain 4.02 %,
Temperature -40.0 °C		 12790 psi
@Strain 4.02 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.00 MPa
@Strain 0.200 %,
Time 36000 sec		 725 psi
@Strain 0.200 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.220 %,
Time 360000 sec		 725 psi
@Strain 0.220 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.260 %,
Time 3.60e+6 sec		 725 psi
@Strain 0.260 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.397 %,
Time 3.60e+7 sec		 725 psi
@Strain 0.397 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.190 %,
Time 3600 sec		 725 psi
@Strain 0.190 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 2.61 %,
Time 3.60e+7 sec		 2900 psi
@Strain 2.61 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  30.0 MPa
@Strain 4.17 %,
Time 3.60e+6 sec		 4350 psi
@Strain 4.17 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
Tensile Strength, Yield  58.0 MPa 8410 psi ISO 527-1/-2
Elongation at Break  40 % 40 % Nominal; ISO 527-1/-2
Elongation at Yield  7.0 % 7.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
  0.2273 GPa
@Temperature 135 °C		 32.97 ksi
@Temperature 275 °F		 Dynamic; ISO 11403-1 -2
  0.242 GPa
@Temperature 120 °C		 35.1 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  0.4473 GPa
@Temperature 75.0 °C		 64.88 ksi
@Temperature 167 °F		 Dynamic; ISO 11403-1 -2
  1.259 GPa
@Temperature 40.0 °C		 182.6 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  1.655 GPa
@Temperature 45.0 °C		 240.0 ksi
@Temperature 113 °F		 Dynamic; ISO 11403-1 -2
  2.621 GPa
@Temperature 5.00 °C		 380.1 ksi
@Temperature 41.0 °F		 Dynamic; ISO 11403-1 -2
  2.783 GPa
@Temperature -20.0 °C		 403.6 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  3.004 GPa
@Temperature -45.0 °C		 435.7 ksi
@Temperature -49.0 °F		 Dynamic; ISO 11403-1 -2
  3.29 GPa
@Temperature -60.0 °C		 477 ksi
@Temperature -76.0 °F		 Dynamic; ISO 11403-1 -2
  3.291 GPa
@Temperature -40.0 °C		 477.3 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Strength  85.0 MPa 12300 psi ISO 178
Flexural Modulus  2.20 GPa 319 ksi ISO 178
Secant Modulus   0.515 GPa
@Strain 6.27 %,
Temperature 40.0 °C		 74.7 ksi
@Strain 6.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.05 GPa
@Strain 2.10 %,
Temperature 40.0 °C		 152 ksi
@Strain 2.10 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.52 GPa
@Strain 0.190 %,
Temperature 40.0 °C		 220 ksi
@Strain 0.190 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.90 GPa
@Strain 4.96 %,
Temperature -40.0 °C		 276 ksi
@Strain 4.96 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.25 GPa
@Strain 1.89 %,
Temperature 23.0 °C		 326 ksi
@Strain 1.89 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.45 GPa
@Strain 3.22 %,
Temperature -40.0 °C		 356 ksi
@Strain 3.22 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.56 GPa
@Strain 1.82 %,
Temperature 0.000 °C		 372 ksi
@Strain 1.82 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.61 GPa
@Strain 2.19 %,
Temperature -20.0 °C		 378 ksi
@Strain 2.19 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.66 GPa
@Strain 0.350 %,
Temperature 23.0 °C		 386 ksi
@Strain 0.350 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.81 GPa
@Strain 0.630 %,
Temperature 0.000 °C		 407 ksi
@Strain 0.630 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.89 GPa
@Strain 1.85 %,
Temperature -40.0 °C		 419 ksi
@Strain 1.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.95 GPa
@Strain 0.860 %,
Temperature -20.0 °C		 428 ksi
@Strain 0.860 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.19 GPa
@Strain 0.790 %,
Temperature -40.0 °C		 463 ksi
@Strain 0.790 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.50 kJ/m² 2.14 ft-lb/in² ISO 180/1A
Izod Impact, Unnotched (ISO)  NB NB ISO 180/1U
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.500 J/cm² 2.38 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   160 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 23200 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  167 MPa
@Pressure 14.0 MPa,
Temperature 110 °C		 24200 psi
@Pressure 2030 psi,
Temperature 230 °F		 ISO 11403-1 -2
  186 MPa
@Pressure 12.0 MPa,
Temperature 110 °C		 27000 psi
@Pressure 1740 psi,
Temperature 230 °F		 ISO 11403-1 -2
  210 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 30500 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  234 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 33900 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  250 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 36300 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  253 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 36700 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  267 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 38700 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  276 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 40000 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  301 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 43600 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  370.37 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 53718 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  391 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 56700 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  400 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 58000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2260 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 327000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2290 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 333000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2350 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 341000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2420 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 351000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2520 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 365000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2630 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 382000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2600 MPa
@Time 3600 sec		 377000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   120 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 17400 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  127 MPa
@Pressure 14.0 MPa,
Temperature 110 °C		 18400 psi
@Pressure 2030 psi,
Temperature 230 °F		 ISO 11403-1 -2
  144.79 MPa
@Pressure 12.0 MPa,
Temperature 110 °C		 21000 psi
@Pressure 1740 psi,
Temperature 230 °F		 ISO 11403-1 -2
  170 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 24700 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  180 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 26100 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  199 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 28900 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  230 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 33300 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  231 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 33500 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  257 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 37300 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  277 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 40100 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  310 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 44900 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  330 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 47900 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  340 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 49300 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  719 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 104000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  869 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 126000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1140 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 166000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1562.5 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 226620 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1790 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 259000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1920 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 279000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+12 ohm 1.00e+12 ohm IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.11 J/g-°C 0.504 BTU/lb-°F  
Thermal Conductivity  0.210 W/m-K 1.46 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  55.0 °C 131 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Fogging 0 mg ISO 6452; G-value (condensate)
Odour class 3 VDA 270; DS
Part Marking Code >PBT< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT  
Thermal desorption analysis of organic emissions 1 µg/g VDA 278; AMax
UL recognition UL  

聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(TPA)或者对苯二甲酸酯(DMT)聚缩合而成，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。

⒈优良的机械性能，机械强度高，耐疲劳性和尺寸稳定好。蠕变也小，这些性能在高温条件下也极少有变化。

⒉生产PBT所消耗的能量是工程塑料中最低的的，这对于世界范围内能源紧缺的情况下，具有十分重要的意义。

⒊耐热老化性优异，增强后的UL温度指数达到120~140℃，此外，户外长期老化性也很好。

⒋耐溶剂好，无应力开裂。

⒌PBT易于阻燃，可达UL94V-0级，由于与阻燃剂亲和性能好，所以容易开发反应型或添加型的阻燃品级。阻燃产品在电子电器工业中获得广泛应用。

⒍PBT遇水易分解，在高温、高湿环境下使用需谨慎。

⒎优良的电气性能，体积电阻率及介电强度高，耐电弧性优良，吸湿性极小，在潮湿及高温环境下，也能保持电性能稳定，是制造电子、电器零件的理想材料。

⒏易成型加工和二次加工，易用普通设备注塑或挤塑。由于结晶速度快，流动性好，模具温度也比其他工程材料要求低，在加工薄壁制件时仅需几秒钟，对大部件也只需40-60s即可。

PBT中文名称聚对苯二甲酸丁酯，简称饱和聚酯，系高结晶性热可塑性塑料。

优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；

3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性极佳。

用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；

2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；

3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。

特点：PBT为乳白色半透明到不透明、结晶型热塑性聚酯。具有高耐热性、韧性、耐疲劳性，自润滑、低摩擦系数，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。PBT 结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套.

上海浩铭塑胶有限公司！本公司承诺，所有产品都是原厂家，原包装一线独家营销！

可提供以下报告：COA（产地证明）SGS（检测报告）MSDS（成分报告）FDA（食品安全报告）UL黄卡（出口报告）正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

联系QQ:996152797

联系邮箱：996152797@qq.com

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40427.html

免责声明: 本文 PBT/美国杜邦/S600F20 NC010 中粘 高流动 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4