LCP S540 材料说明：40%矿物填充级高流量，低翘曲。
LCP S540 加工方法：注塑成型
LCP S540 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.00300 % | 0.00300 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180/1A |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | ISO 75-1, -2 |