杜邦高性能聚合物LW9030 NC010/30%玻纤

杜邦高性能聚合物Crastin ®LW9030 NC010 PBT的+ASA 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT）；PBT + ASA共混，玻璃纤维增强 材料说明：低翘曲的特点增强聚对苯二甲酸丁二醇酯共混物30%玻璃 Crastin LW9030 NC010是30%玻璃纤维增强聚对苯二甲酸乙二醇酯注塑成型的混合。它改善了表面美观性极好的尺寸
 物性表：

 
Physical Properties Metric English Comments
Density  1.28 g/cc 0.0462 lb/in³  
  1.44 g/cc 0.0520 lb/in³ ISO 1183
Water Absorption  0.72 %
@Thickness 2.00 mm		 0.72 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.240 %
@Thickness 2.00 mm		 0.240 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   67000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 67000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  77000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 77000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  89000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 89000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  278000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 278000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  325000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 325000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  383000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 383000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.0015 cm/cm 0.0015 in/in 48h at 80°C; ISO 294-4
  0.0020 cm/cm 0.0020 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.0020 cm/cm 0.0020 in/in 48h at 80°C; ISO 294-4
  0.0070 cm/cm 0.0070 in/in ISO 294-4 2577
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  130 MPa 18900 psi ISO 527-1/-2
Tensile Stress   3.26 MPa
@Strain 0.250 %,
Temperature 160 °C		 473 psi
@Strain 0.250 %,
Temperature 320 °F		 ISO 11403-1 -2
  13.4 MPa
@Strain 1.50 %,
Temperature 160 °C		 1940 psi
@Strain 1.50 %,
Temperature 320 °F		 ISO 11403-1 -2
  17.0 MPa
@Strain 3.00 %,
Temperature 160 °C		 2470 psi
@Strain 3.00 %,
Temperature 320 °F		 ISO 11403-1 -2
  21.8 MPa
@Strain 0.250 %,
Temperature 40.0 °C		 3160 psi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  23.9 MPa
@Strain 0.250 %,
Temperature 23.0 °C		 3470 psi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  25.6 MPa
@Strain 0.250 %,
Temperature 0.000 °C		 3710 psi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  25.9 MPa
@Strain 0.250 %,
Temperature -20.0 °C		 3760 psi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  27.3 MPa
@Strain 0.250 %,
Temperature -40.0 °C		 3960 psi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  95.9 MPa
@Strain 1.50 %,
Temperature 40.0 °C		 13900 psi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  111 MPa
@Strain 1.50 %,
Temperature 23.0 °C		 16100 psi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  125 MPa
@Strain 1.50 %,
Temperature 0.000 °C		 18100 psi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  132 MPa
@Strain 1.50 %,
Temperature -20.0 °C		 19100 psi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  138 MPa
@Strain 1.50 %,
Temperature -40.0 °C		 20000 psi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  10.0 MPa
@Strain 0.105 %,
Time 3600 sec		 1450 psi
@Strain 0.105 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.110 %,
Time 36000 sec		 1450 psi
@Strain 0.110 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  10.0 MPa
@Strain 0.120 %,
Time 360000 sec		 1450 psi
@Strain 0.120 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 0.274 %,
Time 3.60e+6 sec		 2900 psi
@Strain 0.274 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.778 %,
Time 3.60e+6 sec		 7250 psi
@Strain 0.778 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  50.0 MPa
@Strain 0.684 %,
Time 360000 sec		 7250 psi
@Strain 0.684 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  60.0 MPa
@Strain 0.715 %,
Time 3600 sec		 8700 psi
@Strain 0.715 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  60.0 MPa
@Strain 0.757 %,
Time 36000 sec		 8700 psi
@Strain 0.757 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
Elongation at Break  2.5 % 2.5 % ISO 527-1/-2
Tensile Modulus  9.50 GPa 1380 ksi ISO 527-1/-2
  1.441 GPa
@Temperature 160 °C		 209.0 ksi
@Temperature 320 °F		 Dynamic; ISO 11403-1 -2
  6.071 GPa
@Temperature 80.0 °C		 880.5 ksi
@Temperature 176 °F		 Dynamic; ISO 11403-1 -2
  8.992 GPa
@Temperature 30.0 °C		 1304 ksi
@Temperature 86.0 °F		 Dynamic; ISO 11403-1 -2
  9.489 GPa
@Temperature -20.0 °C		 1376 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  9.77 GPa
@Temperature -50.0 °C		 1420 ksi
@Temperature -58.0 °F		 Dynamic; ISO 11403-1 -2
Flexural Strength  190 MPa 27600 psi ISO 178
Flexural Modulus  8.50 GPa 1230 ksi ISO 178
Secant Modulus   2.85 GPa
@Strain 1.50 %,
Temperature 100 °C		 413 ksi
@Strain 1.50 %,
Temperature 212 °F		 ISO 11403-1 -2
  4.03 GPa
@Strain 1.50 %,
Temperature 80.0 °C		 584 ksi
@Strain 1.50 %,
Temperature 176 °F		 ISO 11403-1 -2
  4.40 GPa
@Strain 0.250 %,
Temperature 100 °C		 638 ksi
@Strain 0.250 %,
Temperature 212 °F		 ISO 11403-1 -2
  6.04 GPa
@Strain 0.250 %,
Temperature 80.0 °C		 876 ksi
@Strain 0.250 %,
Temperature 176 °F		 ISO 11403-1 -2
  6.39 GPa
@Strain 1.50 %,
Temperature 40.0 °C		 927 ksi
@Strain 1.50 %,
Temperature 104 °F		 ISO 11403-1 -2
  7.40 GPa
@Strain 1.50 %,
Temperature 23.0 °C		 1070 ksi
@Strain 1.50 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  8.33 GPa
@Strain 1.50 %,
Temperature 0.000 °C		 1210 ksi
@Strain 1.50 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  8.72 GPa
@Strain 0.250 %,
Temperature 40.0 °C		 1260 ksi
@Strain 0.250 %,
Temperature 104 °F		 ISO 11403-1 -2
  8.80 GPa
@Strain 1.50 %,
Temperature -20.0 °C		 1280 ksi
@Strain 1.50 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  9.20 GPa
@Strain 1.50 %,
Temperature -40.0 °C		 1330 ksi
@Strain 1.50 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  9.56 GPa
@Strain 0.250 %,
Temperature 23.0 °C		 1390 ksi
@Strain 0.250 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  10.24 GPa
@Strain 0.250 %,
Temperature 0.000 °C		 1485 ksi
@Strain 0.250 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  10.36 GPa
@Strain 0.250 %,
Temperature -20.0 °C		 1503 ksi
@Strain 0.250 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  10.92 GPa
@Strain 0.250 %,
Temperature -40.0 °C		 1584 ksi
@Strain 0.250 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  8.00 kJ/m² 3.81 ft-lb/in² ISO 180/1A
  8.00 kJ/m²
@Temperature -30.0 °C		 3.81 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1A
Izod Impact, Unnotched (ISO)  50.0 kJ/m² 23.8 ft-lb/in² ISO 180/1U
  50.0 kJ/m²
@Temperature -30.0 °C		 23.8 ft-lb/in²
@Temperature -22.0 °F		 ISO 180/1U
Charpy Impact Unnotched  6.00 J/cm² 28.6 ft-lb/in² ISO 179/1eU
  6.50 J/cm²
@Temperature -30.0 °C		 30.9 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.00 J/cm² 4.76 ft-lb/in² ISO 179/1eA
  0.900 J/cm²
@Temperature -30.0 °C		 4.28 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   1700 MPa
@Pressure 35.0 MPa,
Temperature 120 °C		 246000 psi
@Pressure 5080 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1710 MPa
@Pressure 30.0 MPa,
Temperature 120 °C		 248000 psi
@Pressure 4350 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1730 MPa
@Pressure 25.0 MPa,
Temperature 120 °C		 251000 psi
@Pressure 3630 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1750 MPa
@Pressure 20.0 MPa,
Temperature 120 °C		 253000 psi
@Pressure 2900 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1760 MPa
@Pressure 15.0 MPa,
Temperature 120 °C		 256000 psi
@Pressure 2180 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1780 MPa
@Pressure 10.0 MPa,
Temperature 120 °C		 258000 psi
@Pressure 1450 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1790 MPa
@Pressure 5.00 MPa,
Temperature 120 °C		 259000 psi
@Pressure 725 psi,
Temperature 248 °F		 ISO 11403-1 -2
  7550 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 1.09e+6 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8020 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 1.16e+6 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8390 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 1.22e+6 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  8800 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 1.28e+6 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9090 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 1.32e+6 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9290 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.35e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9440 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.37e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9520 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.38e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  9000 MPa
@Time 3600 sec		 1.31e+6 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   1460 MPa
@Pressure 35.0 MPa,
Temperature 120 °C		 212000 psi
@Pressure 5080 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1470 MPa
@Pressure 30.0 MPa,
Temperature 120 °C		 213000 psi
@Pressure 4350 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1480 MPa
@Pressure 25.0 MPa,
Temperature 120 °C		 214000 psi
@Pressure 3630 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1490 MPa
@Pressure 20.0 MPa,
Temperature 120 °C		 216000 psi
@Pressure 2900 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1500 MPa
@Pressure 15.0 MPa,
Temperature 120 °C		 218000 psi
@Pressure 2180 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1510 MPa
@Pressure 10.0 MPa,
Temperature 120 °C		 219000 psi
@Pressure 1450 psi,
Temperature 248 °F		 ISO 11403-1 -2
  1510 MPa
@Pressure 5.00 MPa,
Temperature 120 °C		 220000 psi
@Pressure 725 psi,
Temperature 248 °F		 ISO 11403-1 -2
  5370 MPa
@Pressure 80.0 MPa,
Temperature 23.0 °C		 779000 psi
@Pressure 11600 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  5830 MPa
@Pressure 70.0 MPa,
Temperature 23.0 °C		 846000 psi
@Pressure 10200 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6200 MPa
@Pressure 60.0 MPa,
Temperature 23.0 °C		 899000 psi
@Pressure 8700 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6430 MPa
@Pressure 50.0 MPa,
Temperature 23.0 °C		 932000 psi
@Pressure 7250 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6670 MPa
@Pressure 40.0 MPa,
Temperature 23.0 °C		 967000 psi
@Pressure 5800 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  6960 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 1.01e+6 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7300 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 1.06e+6 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7550 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 1.09e+6 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  7300 MPa
@Time 3.60e+6 sec		 1.06e+6 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 60093
Dielectric Constant   3.6
@Frequency 1.00e+6 Hz		 3.6
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  36.0 kV/mm 914 kV/in IEC 60243-1
Dissipation Factor   0.0030
@Frequency 100 Hz		 0.0030
@Frequency 100 Hz		 IEC 60250
  0.017
@Frequency 1.00e+6 Hz		 0.017
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  550 V 550 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  25.0 µm/m-°C 13.9 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  100 µm/m-°C 55.6 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  1.90 J/g-°C 0.454 BTU/lb-°F  
Thermal Conductivity  0.260 W/m-K 1.80 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  215 °C 419 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  175 °C 347 °F ISO 75-1/-2
Vicat Softening Point  150 °C 302 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  120 °C 248 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94  HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
Flame Spread  42 mm/min
@Thickness 1.00 mm		 1.7 in/min
@Thickness 0.0394 in		 ISO 3795 (FMVSS 302)
Oxygen Index  19 % 19 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT+ASA-GF30< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT+ASA-GF30  
UL recognition UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40867.html

免责声明: 本文 杜邦高性能聚合物LW9030 NC010/30%玻纤 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4