杜邦高性能聚合物Crastin®s600f20uv wt660聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：增强UV稳定的聚对苯二甲酸乙二醇酯 Crastin S600F20 NC010是一种无筋润滑介质粘度的聚对苯二甲酸乙二醇酯树脂注塑成型。
 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.31 g/cc 0.0473 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   88500 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 88500 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  98730 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 98730 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  109800 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 109800 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  239900 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 239900 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  303800 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 303800 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  384600 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 384600 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  130 cm³/g 130 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.017 cm/cm 0.017 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.016 cm/cm 0.016 in/in ISO 294-4 2577
Melt Flow  19.1 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 19.1 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   2.81 MPa
@Strain 1.14 %,
Temperature 150 °C		 408 psi
@Strain 1.14 %,
Temperature 302 °F		 ISO 11403-1 -2
  2.88 MPa
@Strain 0.190 %,
Temperature 40.0 °C		 418 psi
@Strain 0.190 %,
Temperature 104 °F		 ISO 11403-1 -2
  4.32 MPa
@Strain 1.04 %,
Temperature 90.0 °C		 627 psi
@Strain 1.04 %,
Temperature 194 °F		 ISO 11403-1 -2
  6.84 MPa
@Strain 4.36 %,
Temperature 150 °C		 992 psi
@Strain 4.36 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.06 MPa
@Strain 7.90 %,
Temperature 150 °C		 1310 psi
@Strain 7.90 %,
Temperature 302 °F		 ISO 11403-1 -2
  9.31 MPa
@Strain 0.350 %,
Temperature 23.0 °C		 1350 psi
@Strain 0.350 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  11.7 MPa
@Strain 3.92 %,
Temperature 90.0 °C		 1700 psi
@Strain 3.92 %,
Temperature 194 °F		 ISO 11403-1 -2
  16.07 MPa
@Strain 6.99 %,
Temperature 90.0 °C		 2331 psi
@Strain 6.99 %,
Temperature 194 °F		 ISO 11403-1 -2
  17.7 MPa
@Strain 0.630 %,
Temperature 0.000 °C		 2570 psi
@Strain 0.630 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  18.6 MPa
@Strain 10.5 %,
Temperature 90.0 °C		 2700 psi
@Strain 10.5 %,
Temperature 194 °F		 ISO 11403-1 -2
  21.96 MPa
@Strain 2.10 %,
Temperature 40.0 °C		 3185 psi
@Strain 2.10 %,
Temperature 104 °F		 ISO 11403-1 -2
  25.21 MPa
@Strain 0.790 %,
Temperature -40.0 °C		 3656 psi
@Strain 0.790 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  25.36 MPa
@Strain 0.860 %,
Temperature -20.0 °C		 3678 psi
@Strain 0.860 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  30.59 MPa
@Strain 5.18 %,
Temperature 40.0 °C		 4437 psi
@Strain 5.18 %,
Temperature 104 °F		 ISO 11403-1 -2
  34.8 MPa
@Strain 8.60 %,
Temperature 40.0 °C		 5050 psi
@Strain 8.60 %,
Temperature 104 °F		 ISO 11403-1 -2
  42.45 MPa
@Strain 1.89 %,
Temperature 23.0 °C		 6157 psi
@Strain 1.89 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  46.64 MPa
@Strain 1.82 %,
Temperature 0.000 °C		 6765 psi
@Strain 1.82 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  53.41 MPa
@Strain 1.85 %,
Temperature -40.0 °C		 7746 psi
@Strain 1.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  57.12 MPa
@Strain 2.19 %,
Temperature -20.0 °C		 8285 psi
@Strain 2.19 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  66.69 MPa
@Strain 3.74 %,
Temperature 0.000 °C		 9673 psi
@Strain 3.74 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  73.3 MPa
@Strain 2.85 %,
Temperature -40.0 °C		 10600 psi
@Strain 2.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  78.69 MPa
@Strain 4.18 %,
Temperature -20.0 °C		 11410 psi
@Strain 4.18 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  88.18 MPa
@Strain 4.02 %,
Temperature -40.0 °C		 12790 psi
@Strain 4.02 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  5.00 MPa
@Strain 0.200 %,
Time 36000 sec		 725 psi
@Strain 0.200 %,
Time 10.0 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.220 %,
Time 360000 sec		 725 psi
@Strain 0.220 %,
Time 100 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.260 %,
Time 3.60e+6 sec		 725 psi
@Strain 0.260 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.190 %,
Time 3600 sec		 725 psi
@Strain 0.190 %,
Time 1.00 hour		 isochronous; ISO 11403-1 -2
  5.00 MPa
@Strain 0.397 %,
Time 3.60e+7 sec		 725 psi
@Strain 0.397 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  20.0 MPa
@Strain 2.61 %,
Time 3.60e+7 sec		 2900 psi
@Strain 2.61 %,
Time 10000 hour		 isochronous; ISO 11403-1 -2
  30.0 MPa
@Strain 4.17 %,
Time 3.60e+6 sec		 4350 psi
@Strain 4.17 %,
Time 1000 hour		 isochronous; ISO 11403-1 -2
Tensile Strength, Yield  58.0 MPa 8410 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  7.0 % 7.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
  0.2273 GPa
@Temperature 135 °C		 32.97 ksi
@Temperature 275 °F		 Dynamic; ISO 11403-1 -2
  0.242 GPa
@Temperature 120 °C		 35.1 ksi
@Temperature 248 °F		 ISO 11403-1 -2
  0.4473 GPa
@Temperature 75.0 °C		 64.88 ksi
@Temperature 167 °F		 Dynamic; ISO 11403-1 -2
  1.259 GPa
@Temperature 40.0 °C		 182.6 ksi
@Temperature 104 °F		 ISO 11403-1 -2
  1.655 GPa
@Temperature 45.0 °C		 240.0 ksi
@Temperature 113 °F		 Dynamic; ISO 11403-1 -2
  2.621 GPa
@Temperature 5.00 °C		 380.1 ksi
@Temperature 41.0 °F		 Dynamic; ISO 11403-1 -2
  2.783 GPa
@Temperature -20.0 °C		 403.6 ksi
@Temperature -4.00 °F		 Dynamic; ISO 11403-1 -2
  3.004 GPa
@Temperature -45.0 °C		 435.7 ksi
@Temperature -49.0 °F		 Dynamic; ISO 11403-1 -2
  3.29 GPa
@Temperature -60.0 °C		 477 ksi
@Temperature -76.0 °F		 Dynamic; ISO 11403-1 -2
  3.291 GPa
@Temperature -40.0 °C		 477.3 ksi
@Temperature -40.0 °F		 ISO 11403-1 -2
Flexural Strength  85.0 MPa 12300 psi ISO 178
Flexural Modulus  2.20 GPa 319 ksi ISO 178
Secant Modulus   0.515 GPa
@Strain 6.27 %,
Temperature 40.0 °C		 74.7 ksi
@Strain 6.27 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.05 GPa
@Strain 2.10 %,
Temperature 40.0 °C		 152 ksi
@Strain 2.10 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.52 GPa
@Strain 0.190 %,
Temperature 40.0 °C		 220 ksi
@Strain 0.190 %,
Temperature 104 °F		 ISO 11403-1 -2
  1.90 GPa
@Strain 4.96 %,
Temperature -40.0 °C		 276 ksi
@Strain 4.96 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.25 GPa
@Strain 1.89 %,
Temperature 23.0 °C		 326 ksi
@Strain 1.89 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.45 GPa
@Strain 3.22 %,
Temperature -40.0 °C		 356 ksi
@Strain 3.22 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.56 GPa
@Strain 1.82 %,
Temperature 0.000 °C		 372 ksi
@Strain 1.82 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.61 GPa
@Strain 2.19 %,
Temperature -20.0 °C		 378 ksi
@Strain 2.19 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.66 GPa
@Strain 0.350 %,
Temperature 23.0 °C		 386 ksi
@Strain 0.350 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.81 GPa
@Strain 0.630 %,
Temperature 0.000 °C		 407 ksi
@Strain 0.630 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.89 GPa
@Strain 1.85 %,
Temperature -40.0 °C		 419 ksi
@Strain 1.85 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.95 GPa
@Strain 0.860 %,
Temperature -20.0 °C		 428 ksi
@Strain 0.860 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  3.19 GPa
@Strain 0.790 %,
Temperature -40.0 °C		 463 ksi
@Strain 0.790 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² ISO 180/1A
Charpy Impact, Notched  0.450 J/cm² 2.14 ft-lb/in² ISO 179/1eA
  0.350 J/cm²
@Temperature -30.0 °C		 1.67 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour   160 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 23200 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  167 MPa
@Pressure 14.0 MPa,
Temperature 110 °C		 24200 psi
@Pressure 2030 psi,
Temperature 230 °F		 ISO 11403-1 -2
  186 MPa
@Pressure 12.0 MPa,
Temperature 110 °C		 27000 psi
@Pressure 1740 psi,
Temperature 230 °F		 ISO 11403-1 -2
  210 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 30500 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  234 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 33900 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  250 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 36300 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  253 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 36700 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  267 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 38700 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  276 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 40000 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  301 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 43600 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  370.37 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 53718 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  391 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 56700 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  400 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 58000 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  2260 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 327000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2290 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 333000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2350 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 341000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2420 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 351000 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2520 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 365000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2630 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 382000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  2600 MPa
@Time 3600 sec		 377000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours   120 MPa
@Pressure 15.0 MPa,
Temperature 110 °C		 17400 psi
@Pressure 2180 psi,
Temperature 230 °F		 ISO 11403-1 -2
  127 MPa
@Pressure 14.0 MPa,
Temperature 110 °C		 18400 psi
@Pressure 2030 psi,
Temperature 230 °F		 ISO 11403-1 -2
  144.79 MPa
@Pressure 12.0 MPa,
Temperature 110 °C		 21000 psi
@Pressure 1740 psi,
Temperature 230 °F		 ISO 11403-1 -2
  170 MPa
@Pressure 10.0 MPa,
Temperature 110 °C		 24700 psi
@Pressure 1450 psi,
Temperature 230 °F		 ISO 11403-1 -2
  180 MPa
@Pressure 25.0 MPa,
Temperature 60.0 °C		 26100 psi
@Pressure 3630 psi,
Temperature 140 °F		 ISO 11403-1 -2
  199 MPa
@Pressure 8.00 MPa,
Temperature 110 °C		 28900 psi
@Pressure 1160 psi,
Temperature 230 °F		 ISO 11403-1 -2
  230 MPa
@Pressure 6.00 MPa,
Temperature 110 °C		 33300 psi
@Pressure 870 psi,
Temperature 230 °F		 ISO 11403-1 -2
  231 MPa
@Pressure 20.0 MPa,
Temperature 60.0 °C		 33500 psi
@Pressure 2900 psi,
Temperature 140 °F		 ISO 11403-1 -2
  257 MPa
@Pressure 4.00 MPa,
Temperature 110 °C		 37300 psi
@Pressure 580 psi,
Temperature 230 °F		 ISO 11403-1 -2
  277 MPa
@Pressure 2.00 MPa,
Temperature 110 °C		 40100 psi
@Pressure 290 psi,
Temperature 230 °F		 ISO 11403-1 -2
  310 MPa
@Pressure 15.0 MPa,
Temperature 60.0 °C		 44900 psi
@Pressure 2180 psi,
Temperature 140 °F		 ISO 11403-1 -2
  330 MPa
@Pressure 10.0 MPa,
Temperature 60.0 °C		 47900 psi
@Pressure 1450 psi,
Temperature 140 °F		 ISO 11403-1 -2
  340 MPa
@Pressure 5.00 MPa,
Temperature 60.0 °C		 49300 psi
@Pressure 725 psi,
Temperature 140 °F		 ISO 11403-1 -2
  719 MPa
@Pressure 30.0 MPa,
Temperature 23.0 °C		 104000 psi
@Pressure 4350 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  869 MPa
@Pressure 25.0 MPa,
Temperature 23.0 °C		 126000 psi
@Pressure 3630 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1140 MPa
@Pressure 20.0 MPa,
Temperature 23.0 °C		 166000 psi
@Pressure 2900 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1562.5 MPa
@Pressure 15.0 MPa,
Temperature 23.0 °C		 226620 psi
@Pressure 2180 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1790 MPa
@Pressure 10.0 MPa,
Temperature 23.0 °C		 259000 psi
@Pressure 1450 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1920 MPa
@Pressure 5.00 MPa,
Temperature 23.0 °C		 279000 psi
@Pressure 725 psi,
Temperature 73.4 °F		 ISO 11403-1 -2
  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.11 J/g-°C 0.504 BTU/lb-°F  
Thermal Conductivity  0.210 W/m-K 1.46 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  55.0 °C 131 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Fogging 0 mg ISO 6452; G-value (condensate)
Odour class 3 VDA 270; DS
Part Marking Code >PBT< ISO 11469
Processing Injection Moulding  
Regional Availability North America  
  South and Central America  
Resin Identification PBT  
Special characteristics Light stabilised or stable to light  
Thermal desorption analysis of organic emissions 1 µg/g VDA 278; AMax
 

图：


上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40887.html

免责声明: 本文 杜邦高性能聚合物s600f20uv wt660 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4