LCP 6130l 材料说明：泽尼特«6130l是润滑30%玻璃纤维增强LCP树脂。它非常适合用于汽车，电子，电信，航空航天等行业。
LCP 6130l 加工方法：注塑成型
LCP 6130l 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.80 % | 1.80 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 13.0 GPa | 1890 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz |
4.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.16 @Frequency 2.05e+9 Hz |
4.16 @Frequency 2.05e+9 Hz |
||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 50.0 @Frequency 2.05e+9 Hz |
50.0 @Frequency 2.05e+9 Hz |
||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C | 1.67 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.380 mm |
V-0 @Thickness 0.0150 in |
||