LCP lc-6000 TC 材料说明：热热管理技术™化合物已被工程结合的传热和冷却能力与设计的自由金属，热塑性塑料的减重和成本优势。这些材料提供专有的导电添加剂技术的好处，并选择工程热塑性树脂的性能。热技术的化合物已被证明是提高热导率高达100倍，传统的塑料，可广泛用于热管理中的应用。
LCP lc-6000 TC 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.82 g/cc | 1.82 g/cc | ASTM D792 |
| Water Absorption | 0.010 % @Thickness 3.18 mm |
0.010 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 20.7 GPa | 3000 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.506 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.0 - 10 ohm-cm | 1.0 - 10 ohm-cm | ASTM D257 |
| Surface Resistance | 1.0 - 10 ohm | 1.0 - 10 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C @Thickness 6.35 mm |
540 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C @Thickness 6.35 mm |
531 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 316 - 341 °C | 601 - 646 °F | |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |