| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.272 g/cc | 0.04595 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.026 cm/cm @Thickness 2.00 mm |
0.026 in/in @Thickness 0.0787 in |
ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.023 cm/cm @Thickness 2.00 mm |
0.023 in/in @Thickness 0.0787 in |
ISO 294-4 | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
Resin; ISO 1133 | ||
| 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 482 °F |
Part; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 37.0 MPa @Temperature 23.0 °C |
5370 psi @Temperature 73.4 °F |
ISO 527 | ||
| Tensile Strength, Yield | 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
ISO 527 | ||
| Elongation at Break | 16 % @Temperature 23.0 °C |
16 % @Temperature 73.4 °F |
nominal; ISO 527 | ||
| 20 % @Temperature 23.0 °C |
20 % @Temperature 73.4 °F |
ISO 527 | |||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
ISO 527 | ||
| Tensile Modulus | 2.30 GPa @Temperature 23.0 °C |
334 ksi @Temperature 73.4 °F |
ISO 527 | ||
| Flexural Strength | 65.0 MPa @Temperature 23.0 °C |
9430 psi @Temperature 73.4 °F |
ISO 178 | ||
| Flexural Modulus | 2.015 GPa @Temperature 23.0 °C |
292.3 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Izod Impact, Notched (ISO) | 16.9 kJ/m² @Temperature 23.0 °C |
8.04 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 209 kJ/m² @Temperature 23.0 °C |
99.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | ||
| Charpy Impact Unnotched | 28.0 J/cm² @Temperature 23.0 °C |
133 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | ||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | Optimum | ||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | optimum | ||
| 30.0 - 130 °C | 86.0 - 266 °F | ||||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| De |
|||||
| Drying Recommended | Yes | ||||
| Generic | PBT | ||||
| Product Category | Unreinforced Resins | ||||
| Unreinforced Resins | |||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com