LCP ZE55201 材料说明：泽尼特«ze55201是50%矿物/玻璃纤维增强液晶聚合物注射成型。它是特别适合于要求超平面的应用。
LCP ZE55201 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ISO 1183 |
| Density of Compound | 1.62 g/cc | 0.0585 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.40 % | 1.40 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 15.8 GPa | 2290 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 12.5 GPa | 1810 ksi | ISO 178 |
| Compressive Strength | 21.3 MPa @Strain 1.00 % |
3090 psi @Strain 1.00 % |
ISO 604 |
| Charpy Impact, Notched | 0.360 J/cm² | 1.71 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz |
4.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz |
0.0310 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0310 @Frequency 100 Hz |
0.0310 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C | 8.33 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 300 °C | 572 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||
| Oxygen Index | 41.0 % | 41.0 % | |