| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.170 % | 0.170 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.50 % | 3.50 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 5.80 GPa | 841 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.30 kJ/m² | 2.52 ft-lb/in² | ISO 180/1A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eU |
| 2.20 J/cm² @Temperature -30.0 °C |
10.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 2.90 @Frequency 1.00e+6 Hz |
2.90 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.70 @Frequency 100 Hz |
3.70 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0240 @Frequency 1.00e+6 Hz |
0.0240 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | cavity |
| 250 - 260 °C | 482 - 500 °F | hot runner | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |