| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 | ||
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0500 % @Temperature 22.8 °C |
0.0500 % @Temperature 73.0 °F |
24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.170 % | 0.170 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00600 cm/cm | 0.00300 - 0.00600 in/in | ISO 294-4 | ||
| 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.0110 cm/cm | 0.0110 in/in | ISO 294-4 | ||
| Melt Flow | 9.00 g/10 min @Load 2.16 kg, Temperature 250 °C |
9.00 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm3/10min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 87.0 | 87.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 | ||
| 100 MPa | 14500 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 3.00 % | 3.00 % | 5mm/min; ISO 527-2/1A | ||
| 4.00 % | 4.00 % | ASTM D638 | |||
| Tensile Modulus | 6.70 GPa | 972 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 | ||
| 155 MPa | 22500 psi | ISO 178 | |||
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 | ||
| 6.21 GPa | 900 ksi | ASTM D790 | |||
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | ISO 179/1eU | ||
| 2.80 J/cm² @Temperature -30.0 °C |
13.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz |
3.20 @Frequency 1.00e+6 Hz |
ASTM D150 | ||
| 3.50 @Frequency 1.00e+6 Hz |
3.50 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 3.70 @Frequency 100 Hz |
3.70 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 26.4 kV/mm | 670 kV/in | short term; ASTM D149 | ||
| 30.0 kV/mm | 762 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.00330 @Frequency 100 Hz |
0.00330 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0100 @Frequency 1.00e+6 Hz |
0.0100 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| 0.0160 @Frequency 1.00e+6 Hz |
0.0160 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Arc Resistance | 79.0 sec | 79.0 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 | ||
| 250 V | 250 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 | ||
| 217 °C | 423 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 | ||
| 200 °C | 392 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 8.0 MPa | 95.0 °C | 203 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 206 °C | 403 °F | ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | ISO 11357-1,-2,-3 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
||||
| Oxygen Index | 27.0 - 32.0 % | 27.0 - 32.0 % | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 65.0 - 93.0 °C | 149 - 199 °F | cavity | ||
| 250 - 260 °C | 482 - 500 °F | hot runner | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Processing conditions acc. ISO | 7792-2 | ||||