LCP A410 加工方法：注塑成型
LCP A410 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.84 g/cc | 0.0665 lb/in³ | ISO 1183 |
| Water Absorption | 0.040 % | 0.040 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76 | 76 | ISO 2039-2 |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | IEC 527 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | ISO 178 |
| Compressive Strength | 116 MPa | 16800 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 19.0 GPa | 2760 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | vs. steel; ASTM D1984 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.9 @Frequency 1e+7 Hz |
3.9 @Frequency 1e+7 Hz |
|
| 4.4 @Frequency 1000 Hz |
4.4 @Frequency 1000 Hz |
IEC 250 | |
| Dissipation Factor | 0.0070 @Frequency 1e+7 Hz |
0.0070 @Frequency 1e+7 Hz |
|
| 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
IEC 250 | |
| Arc Resistance | 180 sec | 180 sec | |
| Comparative Tracking Index | 175 V | 175 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 5.00 µm/m-°C @Temperature -50.0 - 200 °C |
2.78 µin/in-°F @Temperature -58.0 - 392 °F |
|
| 5.00 µm/m-°C @Temperature -58.0 - 390 °C |
2.78 µin/in-°F @Temperature -72.4 - 734 °F |
||
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature -50.0 - 200 °C |
36.7 µin/in-°F @Temperature -58.0 - 392 °F |
|
| 66.0 µm/m-°C @Temperature -50.0 - 200 °C |
36.7 µin/in-°F @Temperature -58.0 - 392 °F |
||
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75/A |
| Vicat Softening Point | 235 °C | 455 °F | ASTM D1525 |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Flammability, UL94 | V-0 | V-0 | |