| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 87 | 87 | ISO 2039-2 |
| Tensile Strength at Break | 100 MPa | 14500 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.57 J/cm² | 12.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.540 J/cm² | 2.57 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | Short Term; ASTM D149 |
| 35.0 kV/mm | 889 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0033 @Frequency 100 Hz |
0.0033 @Frequency 100 Hz |
IEC 60250 |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
IEC 60250 | |
| Arc Resistance | 81 sec | 81 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| 260 V | 260 V | ASTM D3638 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 42.0 µm/m-°C @Temperature 20.0 °C |
23.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,2,3 & ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |
| Nozzle Temperature | 250 - 255 °C | 482 - 491 °F | |
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |
| Mold Temperature | 65.0 - 93.0 °C | 149 - 199 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |