拜耳 UT3032 FR橡胶改性PC的共混物,10%的矿物填充

拜耳 UT3032 FR橡胶改性PC的共混物,10%的矿物填充 类别:聚合物;热塑性;聚碳酸酯(PC);聚碳酸酯,影响改性 材料说明:橡胶改性PC共混;10%矿物填充;阻燃剂;挤出级;良好的挤压和真空成型行为;
物性表:
 
Physical Properties Metric English Comments
Density  1.30 g/cc 0.0470 lb/in³ ISO 1183-1
Moisture Absorption at Equilibrium  0.20 % 0.20 % ISO 62, 50% RH
Water Absorption at Saturation  0.50 % 0.50 % ISO 62
Viscosity  380000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C
380000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow  0.0040 - 0.0050 cm/cm
@Thickness 3.00 mm
0.0040 - 0.0050 in/in
@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse  0.0040 - 0.0050 cm/cm
@Thickness 3.00 mm
0.0040 - 0.0050 in/in
@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Melt Flow  13.0 g/10 min
@Load 5.00 kg,
Temperature 260 °C
13.0 g/10 min
@Load 11.0 lb,
Temperature 500 °F
ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  50.0 MPa 7250 psi 50 mm/min; ISO 527-1,-2
Tensile Strength, Yield  63.0 MPa 9140 psi 50 mm/min; ISO 527-1,-2
Elongation at Break  15 % 15 % 50 mm/min; ISO 527-1,-2
Elongation at Yield  4.0 % 4.0 % 50 mm/min; ISO 527-1,-2
Tensile Modulus  3.95 GPa 573 ksi 1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO)   7.00 kJ/m²
@Temperature -30.0 °C
3.33 ft-lb/in²
@Temperature -22.0 °F
ISO 180-A
  9.00 kJ/m²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  48.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
26.7 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow  59.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
32.8 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 1.8 MPa (264 psi)  94.0 °C 201 °F ISO 75-1,-2
Vicat Softening Point   106 °C
@Load 5.10 kg
223 °F
@Load 11.2 lb
50°C/h; ISO 306
  108 °C
@Load 5.10 kg
226 °F
@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94   V-0
@Thickness 0.750 mm
V-0
@Thickness 0.0295 in
 
  5VA
@Thickness 2.00 mm
5VA
@Thickness 0.0787 in
 
  5VA
@Thickness 3.00 mm
5VA
@Thickness 0.118 in
 
 
Processing Properties Metric English Comments
Melt Temperature  260 °C 500 °F Injection molding; ISO 294
Mold Temperature  80.0 °C 176 °F Injection molding; ISO 294
Injection Velocity  240 mm/sec 9.45 in/sec ISO 294
 

图:

上海松翰塑化科技有限公司!本公司承诺,假一赔百!所有产品都是原厂家,原包装一线独家营销!
我司所销售所有产品均为原厂原包,均可提供相关资料报告(如:物性表,MSDS报告,UL报告,COA报告,SGS报告,FDA等)!
欢迎新老客户来电或QQ咨询:
联系人:李生
联系电话;13636696005
联系QQ;1020580970
联系邮箱;1020580970@qq.com
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-41570.html

免责声明: 本文 拜耳 UT3032 FR橡胶改性PC的共混物,10%的矿物填充 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4