Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density
|
1.17
|
g/cm³
|
ISO 1183 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
4400
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break)
|
90.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
4.5
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
3500
|
MPa
|
ISO 178 |
|
Flexural Strength
|
130
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
15
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength (23°C)
|
70
|
kJ/m²
|
ISO 179/1eU |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
230
|
°C
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
> 200
|
°C
|
ISO 306/B |
|
Melting Temperature
|
260
|
°C
|
ISO 11357-3 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80.0
|
°C
|
|
|
Drying Time
|
2.0 to 20
|
hr
|
|
|
Processing (Melt) Temp
|
280 to 300
|
°C
|
|
|
Mold Temperature
|
80.0 to 90.0
|
°C
|