Ultramid® 8232G HS FR BK-102|PA6-GF25|BASF 物性表: Ultramid® 8232G HS FR BK-102|PA6-GF25|BASF物性表及特性介绍,Ultramid® 8232G HS FR BK-102|PA6-GF25|BASF注塑参数详情,如需Ultramid® 8232G HS FR BK-102|PA6-GF25|BASF下载, 可到相关下载区下载

Product TextsUltramid® 8232G HS FR BK102 is a glass fiber reinforced, heat stabilized, flame retardant Polyamid 6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
机械性能(机械性能(Mechanical properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
破坏时应变(Stress at break)145 / -MPaISO 527-1/-2
破坏时应变(Strain at break)2.5 / -%ISO 527-1/-2
热性能(热性能(Thermal properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)220 / *°CISO 11357-1/-3
燃烧性(球压痕硬度(Burning behav)). at thickness hV-0 / *classIEC 60695-11-10
厚度测试(Thickness tested)0.8 / *mmIEC 60695-11-10
UL 识别(recognition)UL / *--
燃烧性(球压痕硬度(Burning behav)). 5V at thickness h5VA / *classIEC 60695-11-20
厚度测试(Thickness tested)2.5 / *mmIEC 60695-11-20
UL 识别(recognition)UL / *--
电气性能(Electrical properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)>1E13 / -Ohm*mIEC 60093
其他属性(Other properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)4 / *%Sim. to ISO 62
吸湿性(Humidity absorption)1.1 / *%Sim. to ISO 62
密度(Density)1620 / *kg/m³ISO 1183
Test specimen production值(Value)单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature275°CISO 294
Injection Molding, mold temperature95°CISO 10724
CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth AmericaOther text informationInjection moldingPREPROCESSING Water content: 0.15% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/wuxingbiao/show-94825.html

免责声明: 本文 Ultramid® 8232G HS FR BK-102|PA6-GF25|BASF 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4