Ultramid® 8202|PA6|BASF物性表报告及物性特性介绍,Ultramid® 8202|PA6|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 8202 is a low viscosity, general purpose Polyamid 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ultramid® 8202 HS) and/or pigmented versions. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2800 / 970	MPa	ISO 527-1/-2
屈服应力(Yield stress)	85 / 36	MPa	ISO 527-1/-2
屈服应变(Yield strain)	4 / 16	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	25 / >50	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N / -	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	51 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	3.5 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	60 / *	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.7 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.5 / -	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3.3 / -	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	0.01 / -	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	0.02 / -	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13 / -	Ohm*m	IEC 60093
相比漏电起痕指数(Comparative tracking index)	- / 600	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	9.5 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2.7 / *	%	Sim. to ISO 62
密度(Density)	1130 / *	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	140 / *	cm³/g	ISO 307, 1157, 1628

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	260	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

Diagrams allowed water content: .15 % Water content: 0.2% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink marks and shri It should be applied and maintained until the gate area is completely frozen off.DisclaimerCopyright M-Base .