Product TextsUltramid® 8202C is a modified crystalline and low viscosity, Polyamid 6 injection molding homopolymer. It is also available in heat stabilized (Ultramid® 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance.
机械性能(机械性能(Mechanical properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)3700 / 1360MPaISO 527-1/-2
屈服应力(Yield stress)88 / 43MPaISO 527-1/-2
屈服应变(Yield strain)4 / 22%ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)7 / >50%ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)N / -kJ/m²ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)3.5 / -kJ/m²ISO 179/1eA
热性能(热性能(Thermal properties))dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)220 / *°CISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)65 / *°CISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness hV-2 / *classIEC 60695-11-10
厚度测试(Thickness tested)0.7 / *mmIEC 60695-11-10
UL 识别(recognition)UL / *--
电气性能(Electrical properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)>1E13 / -Ohm*mIEC 60093
相比漏电起痕指数(Comparative tracking index)- / 600-IEC 60112
其他属性(Other properties)dry / cond单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)9.3 / *%Sim. to ISO 62
吸湿性(Humidity absorption)2.6 / *%Sim. to ISO 62
密度(Density)1130 / *kg/m³ISO 1183
Test specimen production值(Value)单位(Unit)测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature260°CISO 294
Injection Molding, mold temperature80°CISO 10724
CharacteristicsProcessingInjection MoldingDelivery formPelletsRegional AvailabilityNorth AmericaOther text informationInjection moldingPREPROCESSING Water content: 0.2% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. ItDisclaimerCopyright M-Base .

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/wuxingbiao/show-94822.html

免责声明: 本文 Ultramid® 8202C|PA6|BASF 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4