- 密度 [g/cm3]: 0.938
- 拉伸强度 [MPa]: 4.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 13 - 15 % | 13 - 15 % | Arkema | ||
| Melt Index of Compound | 1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 92 | 92 | ASTM D2240 | ||
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 | ||
| 25.0 MPa | 3630 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 4.70 MPa | 682 psi | ASTM D638 | ||
| 5.50 MPa | 798 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 500 - 700 % | 500 - 700 % | Film Property, 50 µm thickness; ASTM D882 | ||
| 700 - 900 % | 700 - 900 % | ASTM D638 | |||
| Dart drop Test | 365 g | 0.805 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 95.0 °C | 203 °F | DSC | ||
| Vicat Softening Point | 71.0 °C | 160 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | >= 200 °C | >= 392 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.7 % | 4.7 % | 50 micron film; ASTM D1003 | ||
| Descriptive Properties | |||||
| MAH Mini | 800 | ||||