- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.94
- 拉伸强度 [MPa]: 5.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 13 - 14 % | 13 - 14 % | |
| Melt Flow | 1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 33.7 | 33.7 | ISO 868 |
| Tensile Strength at Break | 27.7 MPa | 4020 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 5.30 MPa | 769 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 570 % | 570 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0547 GPa | 7.93 ksi | ISO R527 |
| Dart drop Test | 365 g | 0.805 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | D.S.C. method |
| Vicat Softening Point | 70.0 °C | 158 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10.2 % | 10.2 % | 50 micron film; ASTM D1003 |