- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.945
- 拉伸强度 [MPa]: 5.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505 |
| Vinyl Acetate Content | 17 - 20 % | 17 - 20 % | |
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 30.5 | 30.5 | ISO 868 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | 50 microns film; ASTM D882 |
| Tensile Strength, Yield | 5.40 MPa | 783 psi | 50 microns film; ASTM D882 |
| Elongation at Break | 695 % | 695 % | 50 microns film; ASTM D882 |
| Modulus of Elasticity | 0.0379 GPa | 5.50 ksi | ISO R527 |
| Dart drop Test | 250 g | 0.551 lb | 50 microns film |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 85.0 °C | 185 °F | D.S.C. method |
| Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.3 % | 6.3 % | 50 micron film; ASTM D1003 |