- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.938
- 断裂伸长率 [%]: 45.0
- 弯曲强度 [MPa]: 15.0
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ASTM D1505, ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 190/2.16 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 Type IV |
| Elongation at Break | 685 % | 685 % | ASTM D638 Type IV |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | 1% secant, ASTM D790 Method I |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | ASTM D3417 |
| Vicat Softening Point | 59.0 °C | 138 °F | ASTM D1525 |
| Brittleness Temperature | <= -85.0 °C | <= -121 °F | ASTM D746 |