- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.937
- 弯曲模量 [MPa]: 0.0590
- 脆化温度 [℃]: -85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 15 % | 15 % | AT Plastics PTM-39 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 94 | 94 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 725 % | 725 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0590 GPa | 8.56 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 92.0 °C | 198 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 65.0 °C | 149 °F | ASTM D1525 |
| Brittleness Temperature | -85.0 °C | -121 °F | ASTM D746 |