- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 0.933
- 弯曲模量 [MPa]: 0.123
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 9.0 % | 9.0 % | AT Plastics PTM-39 |
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 43 | 43 | ASTM D2240 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 700 % | 700 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.123 GPa | 17.8 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 82.0 °C | 180 °F | ASTM D1525 |