- 熔体流动速率 [g/10min]: 0.5
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.924 g/cc | 0.924 g/cc | ISO 1183 |
| Vinyl Acetate Content | 5.0 % | 5.0 % | Internal Method |
| Thickness | 50.0 - 200 microns | 1.97 - 7.87 mil | Recommended |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ISO 868/A |
| Hardness, Shore D | 44 | 44 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | ISO 527-3 |
| Film Elongation at Break, MD | 450 % | 450 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.6494 g/micron | 67.295 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Dart drop Test | 420 g | 0.926 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 120 MPa | 17400 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 125 MPa | 18100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 °C | 219 °F | Internal Method |
| Vicat Softening Point | 85.0 °C @Load 1.00 kg | 185 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ISO 14782 |
| Gloss | 73 % | 73 % | 45°; ASTM D2457 |