- 熔体流动速率 [g/10min]: 420.0
- 密度 [g/cm3]: 0.941
- 弯曲模量 [MPa]: 0.0131
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 26.7 % | 26.7 % | ExxonMobil Method |
| Melt Flow | 420 g/10 min | 420 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 60 | 60 | 15s; ASTM D2240 |
| Tensile Strength at Break | 1.59 MPa | 230 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.0131 GPa | 1.90 ksi | 1% secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 62.2 °C | 144 °F | Peak Melting Temperature; ExxonMobil Method |