- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.951
- 弯曲模量 [MPa]: 0.0296
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 26.2 % | 26.2 % | ExxonMobil Method | ||
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | 190°C, 2.16 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 82 | 82 | 15s; ASTM D2240 | ||
| Hardness, Shore D | 23 | 23 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 | ||
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 | ||
| Flexural Modulus | 0.0296 GPa | 4.30 ksi | 1% secant; ASTM D790 | ||
| Dart Drop, Total Energy | 21.7 J @Temperature 22.8 °C | 16.0 ft-lb @Temperature 73.0 °F | ASTM D3736 | ||
| 24.4 J @Temperature -40.0 °C | 18.0 ft-lb @Temperature -40.0 °F | ASTM D3736 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 73.9 °C | 165 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||