- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.929
- 拉伸强度 [MPa]: 7.0
- 弯曲强度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength, Ultimate | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D638 |
| Film Elongation at Break, MD | 325 % | 325 % | ASTM D882 |
| Film Elongation at Break, TD | 475 % | 475 % | ASTM D882 |
| Elongation at Break | 1200 % | 1200 % | ASTM D638 |
| Modulus of Elasticity | 0.124 GPa | 18.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.0930 GPa | 13.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.104 GPa | 15.1 ksi | ASTM D882 |
| Dart Drop | 13.0 g/micron | 330 g/mil | ASTM D1709 |
| Dart drop Test | 330 g | 0.728 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 76.0 °C | 169 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.5 % | 4.5 % | ASTM D1003 |
| Gloss | 78 % | 78 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 193 °C | 360 - 379 °F | |